Alloy Tube 30CrNiMo8
时间:2015-11-03 点击:(962)
Alloy pipe is one type of seamless steel pipe. Its chemical composition usually contain more element of Cr. Mo V. Alloy pipe is generally heat treatment. So the performance is better than that of common steel pipes, especially on high temperature resistance, low temperature resistance and corrosion resistance. Alloy pipe is extensively applie to Petroleum, aerospace, chemical industry, power, boiler, military field.
Standard |
Steel Grade |
Tensile strength
(MPa) |
Yielding strength
(MPa) |
Elongation
(%) |
Hardness |
GB3087 |
10 |
335~475 |
≥195 |
≥24 |
/ |
|
20 |
410~550 |
≥245 |
≥20 |
/ |
GB5310 |
20G |
410~550 |
≥245 |
≥24 |
/ |
|
20MnG |
≥415 |
≥240 |
≥22 |
/ |
|
25MnG |
≥485 |
≥275 |
≥20 |
/ |
|
15CrMoG |
440~640 |
≥235 |
≥21 |
/ |
|
12Cr2MoG |
450~600 |
≥280 |
≥20 |
/ |
|
12Cr1MoVG |
470~640 |
≥255 |
≥21 |
/ |
|
12Cr2MoWVTiB |
540~735 |
≥345 |
≥18 |
/ |
|
10Cr9Mo1VNb |
≥585 |
≥415 |
≥20 |
/ |
ASME SA210 |
SA210A-1 |
≥415 |
≥255 |
≥30 |
≤143HB |
|
SA210C |
≥485 |
≥275 |
≥30 |
≤179HB |
ASME SA213 |
SA213 T11 |
≥415 |
≥205 |
≥30 |
≤163HB |
|
SA213 T12 |
≥415 |
≥220 |
≥30 |
≤163HB |
|
SA213 T22 |
≥415 |
≥205 |
≥30 |
≤163HB |
|
SA213 T23 |
≥510 |
≥400 |
≥20 |
≤220HB |
|
SA213 T91 |
≥585 |
≥415 |
≥20 |
≤250HB |
|
SA213 T92 |
≥620 |
≥440 |
≥20 |
≤250HB |
DIN17175 |
ST45.8/Ⅲ |
410~530 |
≥255 |
≥21 |
/ |
|
15Mo3 |
450~600 |
≥270 |
≥22 |
/ |
|
13CrMo44 |
440~590 |
≥290 |
≥22 |
/ |
|
10CrMo910 |
480~630 |
≥280 |
≥20 |
/ |
Standard |
Steel Grade |
Chemical Composition(%) |
|
|
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Cu |
Ni |
V |
Al |
W |
Ti |
Nb |
N |
GB3087 |
10 |
0.07~0.13 |
0.17~0.37 |
0.38~0.65 |
≤0.030 |
≤0.030 |
0.3~0.65 |
/ |
≤0.25 |
≤0.30 |
/ |
/ |
|
|
|
|
|
20 |
0.17~0.23 |
0.17~0.37 |
0.38~0.65 |
≤0.030 |
≤0.030 |
0.3~0.65 |
/ |
≤0.25 |
≤0.30 |
/ |
/ |
|
|
|
|
GB5310 |
20G |
0.17~0.24 |
0.17~0.37 |
0.35~0.65 |
≤0.030 |
≤0.030 |
≤0.25 |
≤0.15 |
≤0.20 |
≤0.25 |
≤0.08 |
|
|
|
|
|
|
20MnG |
0.17~0.24 |
0.17~0.37 |
0.70~1.00 |
≤0.030 |
≤0.030 |
≤0.25 |
≤0.15 |
≤0.20 |
≤0.25 |
≤0.08 |
|
|
|
|
|
|
25MnG |
0.18~0.24 |
0.17~0.37 |
0.80~1.10 |
≤0.030 |
≤0.030 |
≤0.25 |
≤0.15 |
≤0.20 |
≤0.25 |
≤0.08 |
|
|
|
|
|
|
15CrMo |
0.12~0.18 |
0.17~0.37 |
0.40~0.70 |
≤0.030 |
≤0.030 |
0.80~1.10 |
0.40~0.55 |
≤0.20 |
≤0.30 |
|
|
|
|
|
|
|
12Cr2MoG |
0.08~0.15 |
≤0.50 |
0.40~0.70 |
≤0.030 |
≤0.030 |
2.00~2.50 |
0.90~1.20 |
≤0.20 |
≤0.30 |
|
|
|
|
|
|
|
12Cr1MoV |
0.08~0.15 |
0.17~0.37 |
0.40~0.70 |
≤0.030 |
≤0.030 |
0.90~1.20 |
0.25~0.35 |
≤0.20 |
≤0.30 |
0.15~0.30 |
|
|
|
|
|
|
12Cr2MoWVTiB |
0.08~0.15 |
0.45~0.75 |
0.45~0.65 |
≤0.030 |
≤0.030 |
1.60~2.10 |
0.50~0.65 |
≤0.20 |
≤0.30 |
0.28~0.42 |
|
0.30~0.55 |
0.08~0.15 |
B 0.002~0.008 |
|
|
10Cr9Mo1VNb |
0.08~0.12 |
0.20~0.50 |
0.30~0.60 |
≤0.020 |
≤0.010 |
8.00~9.50 |
0.85~1.05 |
≤0.20 |
≤0.40 |
0.18~0.25 |
≤0.015 |
|
|
0.06~0.10 |
0.03~0.07 |
ASME SA210 |
SA210A-1 |
0.13~0.19 |
≥0.1 |
0.45~0.65 |
≤0.030 |
≤0.030 |
|
|
|
|
|
|
|
|
|
|
|
SA210C |
0.18~0.24 |
≥0.1 |
0.80~1.10 |
≤0.030 |
≤0.030 |
|
|
|
|
|
|
|
|
|
|
ASME SA213 |
SA213 T11 |
0.05~0.15 |
0.50~1.0 |
0.30~0.60 |
≤0.030 |
≤0.030 |
1.00~1.50 |
0.50~1.00 |
|
|
|
|
|
|
|
|
|
SA213 T12 |
0.05~0.15 |
≤0.50 |
0.30~0.61 |
≤0.030 |
≤0.030 |
0.80~1.25 |
0.44~0.65 |
|
|
|
|
|
|
|
|
|
SA213 T22 |
0.05~0.15 |
≤0.50 |
0.30~0.60 |
≤0.030 |
≤0.010 |
1.90~2.60 |
0.87~1.13 |
|
|
|
|
|
|
|
|
|
SA213 T23 |
0.04~0.10 |
≤0.50 |
0.10~0.60 |
≤0.030 |
≤0.030 |
1.90~2.60 |
0.05~0.30 |
|
|
|
≤0.030 |
1.45~1.75 |
B 0.0005~0.006 |
0.02~0.08 |
≤0.040 |
|
SA213 T91 |
0.08~0.12 |
0.20~0.50 |
0.30~0.60 |
≤0.020 |
≤0.010 |
8.00~9.50 |
0.85~1.05 |
|
≤0.40 |
0.18~0.25 |
≤0.015 |
|
|
0.06~0.10 |
0.03~0.07 |
|
SA213 T92 |
0.07~0.13 |
≤0.50 |
0.30~0.60 |
≤0.020 |
≤0.010 |
8.50~9.50 |
0.30~0.60 |
|
≤0.40 |
0.15~0.25 |
≤0.015 |
1.50~2.00 |
B 0.001~0.006 |
0.04~0.09 |
0.03~0.07 |
DIN 17175 |
ST45.8/Ⅲ |
≤0.21 |
0.10~0.35 |
0.40~1.20 |
≤0.040 |
≤0.040 |
|
|
|
|
|
|
|
|
|
|
|
15Mo3 |
0.12~0.20 |
0.10~0.35 |
0.40~0.80 |
≤0.035 |
≤0.035 |
|
0.25~0.35 |
|
|
|
|
|
|
|
|
|
13CrMo44 |
0.10~0.18 |
0.10~0.35 |
0.40~0.70 |
≤0.035 |
≤0.035 |
0.70~1.10 |
0.45~0.65 |
|
|
|
|
|
|
|
|
|
10CrMo910 |
0.08~0.15 |
≤0.50 |
0.30~0.70 |
≤0.025 |
≤0.020 |
2.00~2.50 |
0.90~1.10 |
≤0.30 |
≤0.30 |
|
≤0.015 |
|
|
|
|